White-etching matter in bearing steel: Part II: distinguishing cause and effect in bearing steel failure

W. Solano-Alvarez and H. K. D. H. Bhadeshia

Abstract

The premature failure of large bearings of the type used in wind turbines, possibly through a mechanism called ``white-structure flaking", has triggered many studies of microstructural damage associated with "white-etching areas" created during rolling contact fatigue, although whether they are symptoms or causes of failure is less clear. Therefore, some special experiments have been conducted to prove that white-etching areas are the consequence, and not the cause, of damage. By artificially introducing a fine dispersion of microcracks in the steel through heat treatment and then subjecting the sample to rolling contact fatigue, manifestations of hard white-etching matter have been created to a much greater extent than samples similarly tested without initial cracks. A wide variety of characterisation tools has been used to corroborate that the white areas thus created have the same properties as reported observations on real bearings. Evidence suggests that the formation mechanism of the white-etching regions involves the rubbing and beating of the free surfaces of cracks, debonded inclusions, and voids under repeated rolling contact. It follows that the focus in avoiding early failure should be in enhancing the toughness of the bearing steel in order to avoid the initial microscopic feature event.

Metallurgical and Materials Transactions A 45 (2014) 4916-4931.

Download part 2

Download high-resolution images

Download more focused ion beam images

Download archive

Download part 1

Related publications

cracking of bearing steel


Hydrogen TWIP Nuclear growth Maraging steel Bearings Spheroidisation of superbainite
Tempering nanostructures TRIP multipass welds Bainitic powder Shear instabilities Surface hydrogen
Surface displacements Broken bainite Bearing steel Percolation Mn TRIP
Mixed FSW tools Rolling-sliding wear of superbainite Brittle zones Mathematical modelling



PT Group Home Materials Algorithms